5083 Aluminium Sheet
Aluminium 5083 Sheet is known for exceptional performance in extreme environments. 5083 Aluminium Sheetis highly resistant to attack by both seawater and industrial chemical environments.
ASTM B209 5083 Aluminium Sheet also retains exceptional strength after welding. Aluminium Alloy 5083 Sheet has the highest strength of the non-heat treatable alloys but is not recommended for use in temperatures in excess of 65°C.
5083 Aluminium Sheet Temper 0, H32, H34, H38 as per ASTM B209, ASTM-B-209, EN573, and EN485 international standards. O, H111, or H112, UNS A95083, AMS-QQ-A-200/4
Sasa alloy is the leading manufacturer and exporter of 5083 Aluminium Sheet. Supplier of ASTM B209 5083 Aluminium Sheet from 0.5mm to 5mm Thick 1000mm x 1000mm to 2500mm x 1250mm Tempers manufactured in accordance with international standards ASTM B209, ASTM-B-209, EN573, and EN485, check 5083 Aluminium Sheet price. The general widths of 5083 H16 Aluminum sheets are 1000mm, 1250mm and 1500mm, while common lengths are 2000mm, 2500 mm and 3000mm respectively. Wholesale Trader of 5083 Commercial Aluminium Sheet offered by Sasa alloy , China. Stockist of 5083 Aluminium Sheet, H32 5083 Aluminium Stucco Sheet, H38 Commercial 5083 Aluminium Sheet, ASME SB209 5083 Aluminium Patterned Sheet, 5083 Aluminium Embossed Sheet, 5083 Aluminium Extruded Sheet, 5083 Aluminium Sheet and 5083 Aluminium Sheet in China.
Standard Dimensions of 5083 Aluminium Sheet
Standard dimensions (a x b) of Aluminium 5083 Sheet
Aluminium 5083 Sheet up to 9.9 mm
2.000 x 1.000 mm
2.500 x 1.250 mm
3.000 x 1.500 mm
Oversize Aluminium 5083 Sheet
4.000 x 2.000 mm
6.000 x 2.500 mm
8.000 x 2.500 mm
Other dimensions on request
| Alloy | ASTM B209 1050, 1060, 1100, 1235, 3003, 3004, 3105, 5052, 5754, 6061, 8011 |
| Aluminium 5083 Sheet Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| Aluminium 5083 Sheet Thickness | 0.5mm-150mm |
| Aluminium 5083 Sheet Width | 500-2000mm |
| Aluminium 5083 Sheet Length | to clients’ requirement |
| Aluminium 5083 Sheet Coating | Polyester, Fluorocarbon, polyurethane and epoxy coating |
| 5083 Aluminium Sheet Coating finish | PVDF, POLYESTER(PE) |
| Surface | Bright, polished, hair line, brush, sand blast, checkered, embossed, etching, etc. |
| Gloss | Meet the customer requirement |
| Total coating thickness | PVDF coating: More than 25 micron; Polyester coating: More than 18 micron |
| Coating hardness | (pencil hardness) more than 2H |
| Coating adhesive | No lower than1st grade |
| Impact resistance | No cracking or peeling (50kg/cm, ASTMD-2794: 1993) |
| Flexibility (T-bend) | 2T |
| MEK resistance | More than 10 |
| Available Aluminium 5083 Sheet Stock Sizes | 1ft x 1ft, 1ft x 2ft, 1ft x 4ft, 2ft x 2ft, 2ft x 4ft, 4ft x 4ft, 4ft x 8ft, 4ft x 10ft or Cut to Size or Custom Shape. |
| Aluminium 5083 Sheet Delivery Time | 30-60 days after receiving the prepayment |
| Aluminium 5083 Sheet Packaging Details | Standard export package. One pallet is about 2-3 ton.Two steel belts in width and three in width. One 20GP container can load about 18-20 tons Aluminium 5083 Sheet. One 40GP container can load about 24 tons Aluminium 5083 Sheet |
| ASTM B209 Alloy 5083 Outer packing | Export standard, wooden pallet |
| Bottom side Aluminium 5083 Sheet is coated with protective polyester material, thickness more than 6 micron | |
| Export to | Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc. |
5083 Aluminium Sheet Products Show:
| 5083 Aluminium Sheets Product Range | ||||
|---|---|---|---|---|
| Alloy No. | Thickness (mm) |
Width (mm) |
Length (mm) |
Temper |
| A1050, A1060, A1070, A1100 | 0.2-5.0 | 20-2200 | 20-8000 | O, H12, H22, H14, H16, H18, H24, H26 |
| A3003, A3105, A3004 | 0.2-5.0 | 20-2200 | 20-8000 | O, H14, H18, H24 |
| A5052, A5005, A5083, A5086, A5754 | 0.2-5.0 | 20-2200 | 20-8000 | O, H18, H24, H32, H34, H111, H112 |
| A6061, A6082, A6063 | 0.2-5.0 | 20-2200 | 20-8000 | T4, T6, T651 |
| A8011 | 0.2-5.0 | 20-2200 | 20-8000 | O, H12, H22, H14, H16, H18, H24, H26 |
Aluminium 5083 Sheets Manufacturer in China:
1100-H14 Aluminum Sheet: ASTM-B-209
2024-T3 ALCLAD Aluminum Sheet: AMS-QQ-A-205/5, ASTM-B-209, AMS-4041
2024-T3 BARE Aluminum Sheet: AMS-QQ-A-205/5, ASTM-B-209, AMS-4037
2219-T6 Aluminum Sheet:
2219-O Aluminum Sheet: AMS-QQ-A-250/30
3003-H14 Aluminum Sheet: ASTM-B-209
3003-O Aluminum Sheet: ASTM-B-209
4047-F Aluminum Sheet: AMS-4185, BAlSi-4
5052-H32 Aluminum Sheet: ASTM-B-209, AMS-4016
5052-H38 Aluminum Sheet: ASTM-B-209
5052-O Aluminum Sheet: ASTM-B-209, AMS-4015
6061-O Aluminum Sheet: ASTM-B-209, AMS-4025
6061-T4 Aluminum Sheet: ASTM-B-209, AMS-4026
6061-T6 Aluminum Sheet: ASTM-B-209, AMS 4027
7075-T6 Aluminum Sheet: AMS-QQ-A-250/12, AMS-4045
7075-O ALCLAD Aluminum Sheet: ASTM-B-209
7075-O BARE Aluminum Sheet: AMS-QQ-A-250/12, AMS-4045
Aluminum Specular Lighting Sheet
| ALLOYS | SPECIFICATIONS |
|---|---|
| 1100 | AMS-4001, 4003, QQ-A-250/1 |
| 2014-BARE | AMS-4028, 4029 |
| 2014-ALCLAD | QQ-A-250/3 |
| 2024-BARE | AMS-4035,37, QQ-A-250/4 |
| 2024-ALCLAD | AMS-4040, 41, QQ-A-250/5 |
| 2124 | AMS-4101, QQ-A-250/29 |
| 2219 | AMS-4031, 94, 95, QQ-A-250/30 |
| 3003 | AMS-4006, 4008, QQ-A-250/2 |
| 5052 | AMS-4015, 16, 17, QQ-A-250/8 |
| 6013 | AMS-4347, 4216 |
| 6061 | AMS-4025, 26, 27, QQ-A-250/11 |
| 7050 | AMS-4050, 4201, BMS-7-194 |
| 7075-BARE | AMS-4044, 45, QQ-A-250/12 |
| 7075-ALCLAD | AMS-4048, 49, QQ-A-250/13 |
| 7178-BARE | QQ-A-250/14 |
| 7178-ALCLAD | QQ-A-250/15 |
| 7475 | AMS-4084, 4085 |
| Sizes: | .008 to .249 x R/W x R/L .250 to 18.00 x R/W x R/L |
Please note: Other alloys available upon request
* Special Tolerances Available
* Polishing & PVC Protected
Standard Specification of 5083 Aluminium Sheet
Standards and specifications by country
| Specification | Alloy | Temper | Company |
|---|---|---|---|
| Europe | |||
| EN 2089/2395 | 2014A | T6(T62)/T4(T42) | |
| EN 2087/2088 | 2014A clad | T6(T62)/T4(T42) | |
| EN 4101 | 2024 | T4 | |
| EN 2090/2091/2703/4001 | 2024 clad cmq | T3/T4/T4(T42)/T351 | |
| EN 3474/3997/3998/3999 | 2024 cmq | T81/T3/T4(T42)/T351 | |
| EN 2694/EN 3341 | 6061 | T6(T62)/T4(T42) | |
| EN 4449/4450 | 7050 | T76/F(T762) | |
| EN 2696 | 7075 | T6(T62) | |
| EN 2092 | 7075 clad | T6(T62) | |
| EN 2802/3333 | 7475 | T761/F(T762) | |
| EN 2803/3332 | 7475 clad | T761/F(T762) | |
| France | |||
| AIR 9048.010/.030/ | 2014 | F(T42)/F(T62)/T4/ | |
| .020/.040/.050 | 2014 | T6/T451 | |
| AIR 9048.060/.080/.070/.090 | 2014 clad | F(T42)/F(T62)/T4/T6 | |
| AIR 9048.100/.110/.120 | 2024 | ||
| AIR 9048.130/.140 | 2024 clad | F(T42)/T3 | |
| AIR 9048.150 | 2618A | H28(T62) | |
| AIR 9048.170 | 2618A clad | H28(T62) | |
| AIR 9048.190/.200 | 5086 | O, H111/H22, H32 | |
| AIR 9048.210/.220/.230/.240 | 6061 | O, H111(T42)/T4/ O, H111(T62)/T6 | |
| AIR 9048.260/.270 | 7075 | T6/T76 | |
| AIR 9048.280 | 7075 clad | T6 | |
| AIR 9048.290 | 7475 | T76 | Boeing |
| Germany | |||
| W.-Nr. 3.1254 | 2014A | T4, T6 | |
| W.-Nr. 3.1354 | 2024 | O(T42), T3 | |
| W.-Nr. 3.1364 | 2024 clad | O(T42), T3 | |
| W.-Nr. 3.3214 | 6061 | O(T62), T6 | |
| W.-Nr. 3.4364 | 7075 | T6 | |
| W.-Nr. 3.4374 | 7075 clad | O(T62), T6 | |
| W.-Nr. 3.4377 | 7475 clad | T76 | |
| UK | |||
| BS L16/17 | 1200 | H4/O | |
| BS L156/157/158*/159* | 2014A | ||
| 158*/159* | 2014A clad | (T42)(T62) | BAE Systems |
| BS L163/164/165 | 2014A clad | T3/F(T42), T4/T6 | |
| BS L166*/167* | 2014A clad | F(T42), T4/T6 | |
| BS L109/110 | 2024 clad | T3/F(T42) | |
| DTD5070 | 2618A clad | T6 | |
| BS L59/60/61 | 3103 | H6/H2/O | |
| BS L80/81 | 5251 | O/H6 | |
| BS L113 | 6082 | T4, T6 | |
| BS L88 | 7075 clad | T6 | |
| USA | |||
| AMS QQ-A-250/3 | 2014 clad | O, T4, T6 | |
| AMS QQ-A-250/4 | 2024 | O, T3 | |
| AMS 4037 | 2024 | T3 | |
| AMS QQ-A-250/5 | 2024 clad | O, T3 | |
| AMS 4041 | 2024 clad | T3 | |
| AMS QQ-A-250/30 | 2219 | O(T62), T31(T81), T37(T87) | |
| AMS QQ-A-250/2 | 3003 | O, H14 | |
| AMS 4347 | 6013 | T4 | |
| AMS 4216 | 6013 | T6 | |
| AMS 4025/4026/4027 | 6061 | O, F, T4, T42, T45, T6, T62, T651 | |
| AMS QQ-A-250/12 | 7075 | O, T6, T73 | |
| AMS QQ-A-250/24 | 7075 | T76 | |
| AMS QQ-A-250/13 | 7075 clad | O, T6, T73 | |
| AMS QQ-A-250/26 | 7075 clad with 7011 | T76 | |
| AMS QQ-A-250/25 | 7075 clad with 7072 | T76 | |
| European Standard | BS (OLD) | USA (AA) | GERMANY (DIN) | ISO | IS | Canadian |
|---|---|---|---|---|---|---|
| EN AW-1050 A | 1E | 1050 | Al99.5 | Al99.5 | 19500, 19501 | 1 S |
| EN AW-1070 A | – | 1070 | Al-99.7 | Al-99.7 | 19700 | – |
| EN AW-1100 | IC | 1100 | Al-99.0 | Al-99.0 | 19000 | 2 S |
| EN AW-2011 | FC1 | 2011 | AlCuBiPb | AlCu6BiPb | – | 28S |
| EN AW-2014 | HE15 | 2014 | AlCuSiMn | AlCu4SiMg | 24345 | B26S |
| EN AW-2024 | – | 2024 | AlCuMg2 | AlCu4Mg1 | – | 24 S |
| EN AW-3003 | N3 | 3003 | AlMnCu | AlMn1Cu | 31000 | 3 S |
| EN AW-3103 | – | 3103 | – | AlMn1 | – | – |
| EN AW-6101A | E91E | 6101 | E AlMgSi 0.5 | E AlMgSi(A) | 63401 | D50S |
| EN AW-6005 | – | 6005 | AlMgSi0.7 | AlSiMg | 62400 | C51S |
| EN AW-6351 | HE30 | 6351 | AlMgSi1 | AlSiMg0.5Mn | 64430 | B51S |
| EN AW-6060 | – | 6060 | AlMgSi 0.5 | AlMgSi | – | – |
| EN AW-6061 | HE20 | 6061 | AlMgSiCu | AlMg1SiCu | 65032 | 65S |
| EN AW-6063 | HE9 | 6063 | AlMgSi0.5 | AlMg0.7Si | 63400 | 50S |
| EN AW-6082 | HE30 | 6351 | AlMgSi1 | AlSi1MgMn | 64430 | B51S |
5083 Aluminium Sheet Sizes
| Sizes (mm) | Theoretical Mass KG/sheet |
|---|---|
| 2000 X 1000 X 0.5 | 2500 X 1250 X 0.5 |
| 2000 X 1000 X 0.7 | 2500 X 1250 X 0.7 |
| 2000 X 1000 X 0.9 | 2500 X 1250 X 0.9 |
| 2000 X 1000 X 1.2 | 2500 X 1250 X 1.2 |
| 3000 X 1500 X 1.2 | 2000 X 1000 X 1.6 |
| 2500 X 1250 X 1.6 | 3000 X 1500 X 1.6 |
| 2000 X 1000 X 2.0 | 2500 X 1250 X 2.0 |
| 3000 X 1500 X 2.0 | 2500 X 1250 X 2.5 |
| 2.79 | 4.36 |
| 3.91 | 6.10 |
| 5.02 | 7.85 |
| 6.74 | 10.46 |
| 15.01 | 8.93 |
| 13.95 | 20.09 |
| 11.16 | 17.44 |
| 25.11 | 21.80 |
5083 Aluminium Sheet Weight Chart
Width: 1.000 mm | Length: 2.000 mm
| Product | Thickness | Weight |
|---|---|---|
| 5083 Aluminium Sheet | 0,30 mm | 0,810 Kg/m2 |
| 5083 Aluminium Sheet | 0,40 mm | 1,080 Kg/m2 |
| 5083 Aluminium Sheet | 0,50 mm | 1,350 Kg/m2 |
| 5083 Aluminium Sheet | 0,60 mm | 1,620 Kg/m2 |
| 5083 Aluminium Sheet | 0,70 mm | 1,890 Kg/m2 |
| 5083 Aluminium Sheet | 0,80 mm | 2,160 Kg/m2 |
| 5083 Aluminium Sheet | 0,90 mm | 2,430 Kg/m2 |
| 5083 Aluminium Sheet | 1,00 mm | 2,700 Kg/m2 |
| 5083 Aluminium Sheet | 1,20 mm | 3,240 Kg/m2 |
| 5083 Aluminium Sheet | 1,40 mm | 3,780 Kg/m2 |
| 5083 Aluminium Sheet | 1,50 mm | 4,050 Kg/m2 |
| 5083 Aluminium Sheet | 1,60 mm | 4,320 Kg/m2 |
| 5083 Aluminium Sheet | 1,80 mm | 4,860 Kg/m2 |
| 5083 Aluminium Sheet | 2,00 mm | 5,400 Kg/m2 |
| 5083 Aluminium Sheet | 2,20 mm | 5,940 Kg/m2 |
| 5083 Aluminium Sheet | 2,50 mm | 6,750 Kg/m2 |
| 5083 Aluminium Sheet | 3,00 mm | 8,100 Kg/m2 |
| 5083 Aluminium Sheet | 4,00 mm | 10,800 Kg/m2 |
| 5083 Aluminium Sheet | 5,00 mm | 13,500 Kg/m2 |
| 5083 Aluminium Sheet | 6,00 mm | 16,200 Kg/m2 |
| 5083 Aluminium Sheet | 10,00 mm | 27,000 Kg/m2 |
| 5083 Aluminium Sheet | 12,00 mm | 32,400 Kg/m2 |
| 5083 Aluminium Sheet | 15,00 mm | 40,500 Kg/m2 |
| 5083 Aluminium Sheet | 20,00 mm | 54,000 Kg/m2 |
5083 Aluminium Sheet Chemical Composition
| Alloy (ISS) | Equivalent alloy (A.A) | Copper | Magnesium | Silicon | Iron | Managanese Others* (Total) | Remarks | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Old | New | U.S.A | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Max | Max. | Aluminum 99.0% Min. | ||
| N 8 | 54300 | 5083 | — | 0.1 | 4.0 | 4.9 | — | 0.4 | 0.7 | 0.5 | 1.0 | 0.4 | Chromium (0.15-0.35)Either Mn or Cr. shall be present. | ||
Aluminium 5083 Sheet Mechanical Properties
Mechanical Properties of Aluminium Alloy 5083 Sheet
Table 2 (a). Mechanical properties for aluminium alloy 5083 Soft O/H111
| BS EN 485-2:2008 Sheet 0.2 – 6.3mm Thick |
|
|---|---|
| Property | Value |
| Proof Stress | 125 Min MPa |
| Tensile Strength | 275 – 350 MPa |
| Hardness Brinell | 75 HB |
*Properties above are for material in the Soft O/H111 condition
Table 2 (b). Mechanical properties for aluminium alloy 5083 Soft O/H111
| BS EN 485-2:2008 Plate 6.3mm to 80mm |
|
|---|---|
| Property | Value |
| Proof Stress | 115 Min MPa |
| Tensile Strength | 270 – 345 MPa |
| Hardness Brinell | 75 HB |
*Properties above are for material in the Soft O/H111 condition
Table 2 (c). Mechanical properties for aluminium alloy 5083 Soft O/H111
| BS EN 485-2:2008 Plate 80mm to 120mm |
|
|---|---|
| Property | Value |
| Proof Stress | 110 Min MPa |
| Tensile Strength | 260 Min MPa |
| Hardness Brinell | 70 HB |
| Elongation A | 12 Min % |
*Properties above are for material in the Soft O/H111 condition
Table 2 (d). Mechanical properties for aluminium alloy 5083 H32
| BS EN 485-2:2008 Sheet 0.2mm to 6.00mm |
|
|---|---|
| Property | Value |
| Proof Stress | 215 Min MPa |
| Tensile Strength | 305 – 380 MPa |
| Hardness Brinell | 89 HB |
*Properties above are for material in the H32 condition
| Alloy Designation | UK Specifications |
US Specifications |
US Federal Specifications |
European Specifications |
Other |
|---|---|---|---|---|---|
| 7178 A95083 |
AMS 4051 7178-0 Alclad Sheet and Plate | QQ-A-250/15 T0 |
Aluminum Alloy Heat Treatment Temper Designations
Basic Aluminum Heat Treatment Designations
- F As Fabricated
- O Annealed
- H Strain Hardened
- W Solution Heat Treated
- T Solution Heat Treated
Heat Treating T Temper Codes
- T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
- T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
- T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
- T4 – Solution heat treated, and naturally aged to a substantially stable condition.
- T5 – Cooled from an elevated temperature shaping process then artificially aged.
- T6 – Solution heat treated then artificially aged.
- T7 – Solution heat treated then overaged/stabilized.
- T8 – Solution heat treated, cold worked, then artificially aged.
- T9 – Solution heat treated, artificially aged, then cold worked.
- T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.
Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.
H Temper Strain Hardening Codes
- H1 – Strain hardened only
- H2 – Strain hardened and partially annealed
- H3 – Strain hardened and stabilized
- H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.
5083 Packing Information of Aluminum plate :
Application of 5083 Aluminium Sheet
5083 Aluminium Sheet is the most widely used form of Industrial Aluminium. 5083 Aluminium Sheets find applications in various industries such as manufacturing cans and packages, transportation, home appliances, building and construction.