65032 Aluminium Plate
Aluminum 65032 Plate is the least expensive and most versatile of the heat-treatable aluminum alloys. 65032 Aluminum Plate has most of the good qualities of aluminum. It offers a range of good mechanical properties and good corrosion resistance. It can be fabricated by most of the commonly used techniques. In the annealed condition Aluminum Armor Plate 65032 has good workability. In the T4 condition fairly severe forming operations may be accomplished. The full T6 properties may be obtained by artificial aging. It is welded by all methods and can be furnace brazed.
65032 Aluminium Plate ASTM B209, ASTM-B-209, EN573, and EN485 international standards.
AMS 4025 Plate, FED-QQ-A-250/11 – T451, FED-QQ-A-250/11 – T651
Sasa alloy is the leading manufacturer and exporter of 65032 Aluminium Plate. Supplier of ASTM B209 65032 Aluminium Plate from 0.5mm to 5mm Thick 1000mm x 1000mm to 2500mm x 1250mm Tempers manufactured in accordance with international standards ASTM B209, ASTM-B-209, EN573, and EN485, check 65032 Aluminium Plate price. The general widths of 65032 H16 Aluminum Plates are 1000mm, 1250mm and 1500mm, while common lengths are 2000mm, 2500 mm and 3000mm respectively. Wholesale Trader of 65032 Commercial Aluminium Plate offered by Sasa alloy , China. Stockist of 65032 Aluminium Plate, H32 65032 Aluminium Stucco Plate, H38 Commercial 65032 Aluminium Plate, ASME SB209 65032 Aluminium Patterned Plate, 65032 Mill Finish, 65032 Aluminium Extruded Plate, 65032 Aluminium Plate and 65032 Aluminium Plate in China.
65032 Aluminium Plate Suppliers in UNS A965032 Aluminium Plate stockist in China, 65032 Aluminium Corrugated Plate Suppliers in Best Price of EN AW 65032 H14 Aluminium Plate
You may intrested in:
- 65032 Aluminium Chequered Plate
- 65032 Aluminium Checker Plate
- 65032 Aluminium Diamond Plate
- 65032 Aluminium Tread Plate
- 6061-O Aluminum Plate: ASTM-B-209, AMS-4025
- 6061-T4 Aluminum Plate: ASTM-B-209, AMS-4026
- 6061-T6 Aluminum Plate: ASTM-B-209, AMS 4027
Standard Dimensions of 65032 Aluminium Plate
Standard dimensions (a x b) of Aluminium 65032 Plate
Aluminium 65032 Plate up to 9.9 mm
2.000 x 1.000 mm
2.500 x 1.250 mm
3.000 x 1.500 mm
Oversize Aluminium 65032 Plate
4.000 x 2.000 mm
6.000 x 2.500 mm
8.000 x 2.500 mm
Other dimensions on request
65032 Aluminium Plate Suppliers in China, 65032 Aluminium Plate Supplier Singapore, Dealer & Distributor of All 65032 Aluminium Alloy Plate Grades, Stockholder of 65032 Aluminium Plate 1mm
Aluminium Alloy | ASTM B209 65032 |
Aluminium 65032 Plate Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
Aluminium 65032 Plate Thickness | 0.5mm-150mm |
Aluminium 65032 Plate Width | 500-2000mm |
Aluminium 65032 Plate Length | to clients’ requirement |
Aluminium 65032 Plate Coating | Polyester, Fluorocarbon, polyurethane and epoxy coating |
65032 Aluminium Plate Coating finish | PVDF, POLYESTER(PE) |
Aluminium 65032 Plate Surface | Polished, hair line, brush, sand blast, checkered, embossed, etching, etc. Mill finish, Bright finish, paper interleaved, one side film, both sides film. |
Aluminium 65032 Plate Gloss | Meet the customer requirement |
Total coating thickness of Aluminium 65032 Plate | PVDF coating: More than 25 micron; Polyester coating: More than 18 micron |
Aluminium 65032 Plate Coating hardness | (pencil hardness) more than 2H |
Aluminium 65032 Plate Coating adhesive | No lower than1st grade |
Aluminium 65032 Plate Impact resistance | No cracking or peeling (50kg/cm, ASTMD-2794: 1993) |
Aluminium 65032 Plate Flexibility (T-bend) | 2T |
Aluminium 65032 Plate MEK resistance | More than 10 |
Available Aluminium 65032 Plate Stock Sizes | 1ft x 1ft, 1ft x 2ft, 1ft x 4ft, 2ft x 2ft, 2ft x 4ft, 4ft x 4ft, 4ft x 8ft, 4ft x 10ft or Cut to Size or Custom Shape. |
Aluminium 65032 Plate Delivery Time | 30-60 days after receiving the prepayment |
Aluminium 65032 Plate Packaging Details | Standard export package. One pallet is about 2-3 ton.Two steel belts in width and three in width. One 20GP container can load about 18-20 tons Aluminium 65032 Plate. One 40GP container can load about 24 tons Aluminium 65032 Plate |
ASTM B209 Alloy 65032 Plate Outer packing | Export standard, wooden pallet |
Bottom side Aluminium 65032 Plate is coated with protective polyester material, thickness more than 6 micron | |
We Export Aluminium 65032 Plate to | Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc. |
AUTHORIZED DISTRIBUTORS OF , NALCO, , THYSSENKRUPP, VIRGO, MANKASIA AND METENERE |
Types of 65032 Aluminium Plate Manufacturer in China
65032 Aluminium Plates Product Range | ||||
---|---|---|---|---|
Alloy No. | Thickness (mm) |
Width (mm) |
Length (mm) |
Temper |
65032 Aluminium Plate | 0.2-5.0 | 20-2200 | 20-8000 | O, H12, H22, H14, H16, H18, H24, H26 |
Standard Specification of 65032 Aluminium Plate
Standards and specifications by country
Specification | Alloy | Temper | Company |
---|---|---|---|
Europe | |||
EN 2694/EN 3341 | 6061 | T6(T62)/T4(T42) | |
AIR 9048.210/.220/.230/.240 | 6061 | O, H111(T42)/T4/ O, H111(T62)/T6 | |
W.-Nr. 3.3214 | 6061 | O(T62), T6 | |
AMS 4025/4026/4027 | 6061 | O, F, T4, T42, T45, T6, T62, T651 |
European Standard | BS (OLD) | USA (AA) | GERMANY (DIN) | ISO | IS | Canadian |
---|---|---|---|---|---|---|
EN AW-6061 | HE20 | 6061 | AlMgSiCu | AlMg1SiCu | 65032 | 65S |
65032 Aluminium Plate Sizes
Sizes (mm) | Theoretical Mass KG/Plate |
---|---|
2000 X 1000 X 0.5 | 2500 X 1250 X 0.5 |
2000 X 1000 X 0.7 | 2500 X 1250 X 0.7 |
2000 X 1000 X 0.9 | 2500 X 1250 X 0.9 |
2000 X 1000 X 1.2 | 2500 X 1250 X 1.2 |
3000 X 1500 X 1.2 | 2000 X 1000 X 1.6 |
2500 X 1250 X 1.6 | 3000 X 1500 X 1.6 |
2000 X 1000 X 2.0 | 2500 X 1250 X 2.0 |
3000 X 1500 X 2.0 | 2500 X 1250 X 2.5 |
2.79 | 4.36 |
3.91 | 6.10 |
5.02 | 7.85 |
6.74 | 10.46 |
15.01 | 8.93 |
13.95 | 20.09 |
11.16 | 17.44 |
25.11 | 21.80 |
65032 Aluminium Plate Weight Chart
Width: 1.000 mm | Length: 2.000 mm
Product | Thickness | Weight |
---|---|---|
65032 Aluminium Plate | 0,30 mm | 0,810 Kg/m2 |
65032 Aluminium Plate | 0,40 mm | 1,080 Kg/m2 |
65032 Aluminium Plate | 0,50 mm | 1,350 Kg/m2 |
65032 Aluminium Plate | 0,60 mm | 1,620 Kg/m2 |
65032 Aluminium Plate | 0,70 mm | 1,890 Kg/m2 |
65032 Aluminium Plate | 0,80 mm | 2,160 Kg/m2 |
65032 Aluminium Plate | 0,90 mm | 2,430 Kg/m2 |
65032 Aluminium Plate | 1,00 mm | 2,700 Kg/m2 |
65032 Aluminium Plate | 1,20 mm | 3,240 Kg/m2 |
65032 Aluminium Plate | 1,40 mm | 3,780 Kg/m2 |
65032 Aluminium Plate | 1,50 mm | 4,050 Kg/m2 |
65032 Aluminium Plate | 1,60 mm | 4,320 Kg/m2 |
65032 Aluminium Plate | 1,80 mm | 4,860 Kg/m2 |
65032 Aluminium Plate | 2,00 mm | 5,400 Kg/m2 |
65032 Aluminium Plate | 2,20 mm | 5,940 Kg/m2 |
65032 Aluminium Plate | 2,50 mm | 6,750 Kg/m2 |
65032 Aluminium Plate | 3,00 mm | 8,100 Kg/m2 |
65032 Aluminium Plate | 4,00 mm | 10,800 Kg/m2 |
65032 Aluminium Plate | 5,00 mm | 13,500 Kg/m2 |
65032 Aluminium Plate | 6,00 mm | 16,200 Kg/m2 |
65032 Aluminium Plate | 10,00 mm | 27,000 Kg/m2 |
65032 Aluminium Plate | 12,00 mm | 32,400 Kg/m2 |
65032 Aluminium Plate | 15,00 mm | 40,500 Kg/m2 |
65032 Aluminium Plate | 20,00 mm | 54,000 Kg/m2 |
65032 Aluminium Plate Chemical Composition
Alloy (ISS) | Equivalent alloy (A.A) | Copper | Magnesium | Silicon | Iron | Managanese Others* (Total) | Remarks | ||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Old | New | U.S.A | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Max | Max. | Aluminum 99.0% Min. | ||
H 20 | 65032 | 6061 | 0.15 | 0.4 | 0.7 | 1.2 | 0.4 | 0.8 | 0.7 | 0.2 | 0.8 | 0.4 | Chromium up to 0.10 |
Aluminium 65032 Plate Mechanical Properties
Plate (according to the standard EN 485-2):
State
|
Specified thickness (mm)
|
Rm (MPa)
|
Rp0,2 (MPa)
|
A % mini
|
Bending radius
|
Hardness HBS
|
|||||
---|---|---|---|---|---|---|---|---|---|---|---|
More than
|
until
|
mini
|
maxi
|
mini
|
maxi
|
A 50
|
A
|
180°
|
90°
|
||
O
|
>0,41,53,06,012,5 | 1,53,06,012,525,0 |
–
|
150150150150150 |
–
|
8585858585 | 14161916 | 16 | 1,0 e1,0 e | 0,5 e1,0 e1,0 e2,0 e | 4040404040 |
T4T 451 | > 0,41,53,06,0 | 1,53,06,012,5 | 205205205205 |
–
|
110110110110 |
–
|
–
|
12141618 | 1,5 e2,0 e | 1,0 e1,5 e3,0 e4,0 e | 58585858 |
T451
|
12,540,0 | 40,080,0 | 205205 |
–
|
110110 |
–
|
–
|
15.14 |
–
|
–
|
5858 |
T42
|
>0,41,53,06,012,540,0 | 1,53,06,012,540,080,0 |
205 205 205 205 205 205 |
– |
95 95 95 95 95 95 |
– | 12141618 | 1514 | – | 1,0 e1,5 e3,0 e4,0 e | 575757575757 |
T6T651T62 | > 0,41,53,06,0 | 1,53,06,012,5 | 290290290290 |
–
|
240240240240 |
–
|
–
|
67109 | – | 2,5 e3,5 e4,0 e5,0 e | 88888888 |
T651 T62 |
12,540,080,0100,0150,0 | 40,080,0100,0150,0175,0 |
290 290 290 275 265 |
– |
240 240 240 240 230 |
– | – | 86554 | – | – | 8888888481 |
Aluminum Alloy Heat Treatment Temper Designations
Basic Aluminum Heat Treatment Designations
- F As Fabricated
- O Annealed
- H Strain Hardened
- W Solution Heat Treated
- T Solution Heat Treated
Heat Treating T Temper Codes for Aluminium 65032 Plates
- T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
- T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
- T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
- T4 – Solution heat treated, and naturally aged to a substantially stable condition.
- T5 – Cooled from an elevated temperature shaping process then artificially aged.
- T6 – Solution heat treated then artificially aged.
- T7 – Solution heat treated then overaged/stabilized.
- T8 – Solution heat treated, cold worked, then artificially aged.
- T9 – Solution heat treated, artificially aged, then cold worked.
- T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.
Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.
H Temper Strain Hardening Codes for Aluminium 65032 Plates
- H1 – Strain hardened only
- H2 – Strain hardened and partially annealed
- H3 – Strain hardened and stabilized
- H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.
65032 Plate Packing Information of Aluminum plate :
Application of 65032 Aluminium Plate
65032 Aluminium Plate is the most widely used form of Industrial Aluminium. 65032 Aluminium Plates find applications in various industries such as manufacturing cans and packages, transportation, home appliances, building and construction.